EN 13245-1:2010

2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Kunststoffe - Profile aus weichmacherfreiem Poly(vinylchlorid) (PVC-U) für die Anwendung im Bauwesen - Teil 1: Bezeichnung von PVC-U ProfilenPlastiques - Profilés en poly(chlorure de vinyle) non plastifié (PVC-U) pour applications dans le bâtiment - Partie 1: Désignation des profilés en PVC-UPlastics - Unplasticized poly(vinyl chloride) (PVC-U) profiles for building applications - Part 1: Designation of PVC-U profiles83.140.99Drugi izdelki iz gume in polimernih materialovOther rubber and plastics productsICS:Ta slovenski standard je istoveten z:EN 13245-1:2010SIST EN 13245-1:2010en,fr,de01-september-2010SIST EN 13245-1:2010SLOVENSKI
STANDARDSIST EN 13245-1:20051DGRPHãþD

EUROPEAN STANDARD NORME EUROPÉENNE EUROPÄISCHE NORM
EN 13245-1
June 2010 ICS 83.140.99 Supersedes EN 13245-1:2004English Version
Plastics - Unplasticized poly(vinyl chloride) (PVC-U) profiles for building applications - Part 1: Designation of PVC-U profiles
Plastiques - Profilés en poly(chlorure de vinyle) non plastifié(PVC-U) pour applications dans le bâtiment - Partie 1: Désignation des profilés en PVC-U
Kunststoffe - Profile aus weichmacherfreiem Polyvinylchlorid (PVC-U) für die Anwendung im Bauwesen -Teil 1: Bezeichnung von Profilen aus PVC-U This European Standard was approved by CEN on 19 May 2010.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre:
Avenue Marnix 17,
B-1000 Brussels © 2010 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 13245-1:2010: ESIST EN 13245-1:2010

Determination of the linear mass . 16A.1 Apparatus . 16A.2 Test specimens . 16A.3 Procedure . 16A.4 Calculation and expression of results . 16Annex B (normative)
Determination of the impact resistance . 17B.1 Principle . 17B.2 Apparatus . 17B.3 Test specimens . 17B.4 Conditioning . 18B.5 Procedure . 18B.6 Expression of results . 19Annex C (normative)
Determination of peel strength . 20C.1 Principle . 20C.2 Apparatus . 20C.3 Preparation of test pieces . 21C.4 Conditioning . 21C.5 Procedure . 21C.6 Test report . 22Bibliography . 23 SIST EN 13245-1:2010

Unplasticized poly(vinyl chloride) (PVC-U) profiles for building applications, consists of the following parts:  Part 1: Designation of PVC-U profiles  Part 2: PVC-U profiles and PVC-UE profiles for internal and external wall and ceiling finishes  Part 3: Designation of PVC-UE profiles It is a revision of EN 13245-1:2004 with the extension of the scope to:  light coloured PVC-U profiles with or without a laminated foil or a lacquered-coating;  coloured PVC-U profiles, obtained by a mono-extrusion or a co-extrusion process, with or without laminated foil or with
lacquered-coating. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. SIST EN 13245-1:2010

It specifies test methods and test parameters.
This method of designation is intended to be used in product specification when the application is specified. NOTE It is recommended to use this method for the designation of PVC-U profiles for information related to technical literature of the manufacturer, not for the marking of the products. Profiles for the management of electrical power cables, communication cables and power track systems used for the distribution of electrical power, profiles for windows or doors and profiles for guttering are not covered by this European Standard.1) 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 438-2:2005, High-pressure decorative laminates (HPL) — Sheets based on thermosetting resins (usually called Laminates) — Part 2: Determination of properties EN 477:1995, Unplasticized polyvinylchloride (PVC-U) profiles for the fabrication of windows and doors — Determination of the resistance to impact of main profiles by falling mass EN 478, Unplasticized polyvinylchloride (PVC-U) profiles for the fabrication of windows and doors — Appearance after exposure at 150 °C — Test method EN 479, Unplasticized polyvinylchloride (PVC-U) profiles for the fabrication of windows and doors — Determination of heat reversion EN 513:1999, Unplasticized polyvinylchloride (PVC-U) profiles for the fabrication of windows and doors — Determination of the resistance to artificial weathering EN 20105-A02, Textiles — Tests for colour fastness — Part A02: Grey scale for assessing change in colour (ISO 105-A02:1993)
EN ISO 105-A01:2010, Textiles — Tests for colour fastness — Part A01: General principles of testing (ISO 105-A01:2010) EN ISO 178, Plastics — Determination of flexural properties (ISO 178:2001) EN ISO 306:2004, Plastics — Thermoplastic materials — Determination of Vicat softening temperature (VST) (ISO 306:2004) EN ISO 472:2001, Plastics — Vocabulary (ISO 472:1999)
1) Profiles that are excluded are in the scopes of standards prepared by CEN/TC 33, CENELEC/TC 213 or CEN/TC 128. SIST EN 13245-1:2010

EN ISO 1043-1:2001 and the following apply. 3.1 PVC-U profile profile made of unplasticized poly(vinyl chloride) (PVC-U) material NOTE It applies to profiles made of non-cellular material as opposed to cellular material. 3.2 Type of profile
3.2.1 Type 1 profile PVC-U profile obtained by a mono-extrusion process (coloured in the mass) 3.2.2 Type 2 profile PVC-U profile obtained by a co-extrusion process 3.2.3 Type 3 profile PVC-U profile as Type 1 or Type 2 with laminated foil 3.2.4 Type 4 profile PVC-U profile as Type 1 or Type 2 with lacquer-coating 3.3 sight surface surface of a profile that is exposed to view, when the PVC-U profile is installed SIST EN 13245-1:2010

covering layer on the sight surface of a PVC-U profile, e.g. a co-extruded layer, a lacquer-coating or a laminated foil 3.5 laminated foil plastic layer bonded with an adhesive or under pressure and temperature to cover a surface of a PVC-U profile 3.6 co-extrusion
durable bonding of two thermoplastics [e.g. unplasticized polyvinylchloride (PVC-U) and poly(methyl methacrylate) (PMMA)] that are melted in separated extruders and fused together in the profile tool 3.7 lacquer-coating one or several layer(s) of lacquer (e.g. acrylic or polyurethane resin) or varnish (clear coating material) that cover(s) a PVC-U profile 3.8 radiant exposure time integral of irradiance, measured in joules per square metre (J/m−2) [ISO 9370:2009] 4 Designation of PVC-U profiles The PVC-U profiles are designated in accordance with a classification system of their characteristics. The designation consists of a description block and five data blocks as given in Table 1. SIST EN 13245-1:2010

For types of profiles
See 3.2 Data block 2: Intended application One or more following codes depending on the intended application:
For outside building applications:
E For inside building applications:
I Data block 3: Material properties Vicat softening temperature (VST):
See 5.1 Modulus of elasticity in flexure:
See 5.2 Data block 4: Profile properties Nominal linear mass:
See 5.3 Heat reversion at 100 °C:
See 5.4 Impact resistance:
See 5.5 Data block 5: Durability See 5.6 a For Type 3 or Type 4 profiles, the requirements given in 6.1 to 6.4 shall be fulfilled, as applicable. 5 Codification system for Data block 3 to Data block 5 5.1 Vicat softening temperature (Data block 3) The Vicat softening temperature (VST) shall be measured in accordance with EN ISO 306:2004, Method B50, using 4 mm thick test specimens, prepared according to EN ISO 1163-2, as indicated in Table 2.
Table 2 — Preparation of test specimens Type of profile Compound to be tested Type 1 PVC-U compound Type 2, Type 3 and Type 4 Each of the extruded compounds, as applicable
The value of VST shall be coded according to Table 3. For Type 2, Type 3 and Type 4 profiles, as applicable, the values of the VST of each compound shall be coded from the internal layer to the external layer, with a separation by "/". 5.2 Modulus of elasticity in flexure (Data block 3) The modulus of elasticity in flexure, E, shall be measured in accordance with EN ISO 178, using a 4 mm thick test specimens prepared according to EN ISO 1163-2, as indicated in Table 2. For Type 2, Type 3 and Type 4 profiles, as applicable, the values of the modulus of elasticity in flexure of each compound shall be coded from the internal layer to the external layer, with a separation by "/". The value of the modulus of elasticity in flexure shall be coded according to Table 3.
Vicat softening temperature (VST) Modulus of elasticity in flexure, E Range of values MPa Code The VST is represented by three figures giving the softening temperature. E.g. code 082 for a nominal VST value of
82 °C.
1 700 < E < 2 000 2 000 < E < 2 300 2 300 < E < 2 600 2 600 < E < 2 900 2 900 < E < 3 200 3 200 < E < 3 500 (1 700 + 300 × n) < E < (2 000 + 300 × n) a 17 20 23 26 29 32 "(17 + 3 × n)" a n is an integer.
5.3 Nominal linear mass (Data block 4) The nominal linear mass of the PVC-U profile shall be measured in accordance with Annex A. The value of the nominal linear mass shall be coded according to Table 4. 5.4 Heat reversion at 100 °C (Data block 4) The heat reversion at 100 °C of the PVC-U profile, R, shall be measured in accordance with EN 479. The value of the heat reversion at 100 °C shall be coded according to Table 4. 5.5 Impact resistance (Data block 4) The impact resistance of the PVC-U profile at 23 °C or, if required, at a low temperature (0 °C, - 10 °C, - 20 °C or - T' °C), shall be measured in accordance with Annex B. The value of the impact resistance shall be coded according to Table 4. SIST EN 13245-1:2010

Nominal linear mass, PM Heat reversion at 100 °C Impact resistance at
T °C R % Code
Energy level J Code The nominal linear mass is represented by four figures giving the nominal linear mass. E.g. code 1483 for a nominal linear mass of 1 483 g/m. R ≤ 2 R ≤ 3 R ≤ n a
2 3 n
1 2 3 4 5 6 10 15 20 "(5 × m)" b (T,01) (T,02) (T,03) (T,04) (T,05) (T,06) (T,10) (T,15) (T,20) "[ T,(5 × m)]" a n is an integer. b m is an integer.
EXAMPLES
− Code (23,10) for a PVC-U profile with an impact resistance at 23 °C of 10 J; − Code (-20,05) for a PVC-U profile with an impact resistance at - 20 °C of 5 J. 5.6 Durability (Data block 5) 5.6.1 General Assessment of the durability is based on the following criteria: a) The colour differences between unexposed and exposed PVC-U profiles; b) The tensile-impact strength of the PVC-U profiles after ageing; c) The visual inspection of the PVC-U profiles after ageing; d) The adhesion of the coating of the PVC-U profiles after ageing (for Type 3 and Type 4 profiles, only). 5.6.2 Test methods for ageing 5.6.2.1 Outside building applications Ageing shall be carried out according to either an artificial ageing test method or a natural ageing test method. a) Artificial ageing test method according to EN 513:1999, Method 1 (referring to EN ISO 4892-2:2006, Method A). The conditions shall be defined in accordance with the code "A.n.T", where: 1) A means "artificial ageing"; SIST EN 13245-1:2010

is the radiant exposure received by the exposed specimen, expressed in gigajoules per square metre, in the wavelength range 290 nm to 800 nm; 3) T is the black standard temperature (BST), if other than (60 ± 3) °C, as specified in EN 513:1999. EXAMPLE i) Codes A.8, A.12: a radiant exposure of 8 GJ/m² and 12 GJ/m² respectively, and a black standard temperature of 60 °C; ii) Code A.8.55: a radian
...